ALUMINUM 5052-O Subcategory: 5000 Series Aluminum Alloy; Aluminum Alloy; Metal; Nonferrous Metal Close Analogs: Composition Notes: Aluminum content reported is calculated as remainder. Composition information provided by the Aluminum Association and is not for design. Key Words: UNS A95052; ISO AlMg2.5; Aluminium 5052-O; AA5052-O Component Wt. % Al95.7 - 97.7 Cr0.15 - 0.35 CuMax 0.1 FeMax 0.4 Component Wt. % Mg2.2 - 2.8 MnMax 0.1 Other, eachMax 0.05 Component Wt. % Other, totalMax 0.15 SiMax 0.25 ZnMax 0.1 Material Notes: Data points with the AA note have been provided by the Aluminum Association, Inc. and are NOT FOR DESIGN. Physical PropertiesMetricEnglishComments Density2.68 g/cc0.0968 lb/in³ AA; Typical Mechanical Properties Hardness, Brinell4747 AA; Typical; 500 g load; 10 mm ball Ultimate Tensile Strength193 MPa28000 psi AA; Typical Tensile Yield Strength89.6 MPa13000 psi AA; Typical Elongation at Break25 %25 % AA; Typical; 1/16 in. (1.6 mm) Thickness Elongation at Break30 %30 % AA; Typical; 1/2 in. (12.7 mm) Diameter Modulus of Elasticity70.3 GPa10200 ksi AA; Typical; Average of tension and compression. Compression modulus is about 2% greater than tensile modulus. Ultimate Bearing Strength345 MPa50000 psi Edge distance/pin diameter = 2.0 Bearing Yield Strength131 MPa19000 psi Edge distance/pin diameter = 2.0 Poisson's Ratio0.330.33 Fatigue Strength110 MPa16000 psi AA; 500,000,000 cycles completely reversed stress; RR Moore machine/specimen Machinability30 %30 % 0-100 Scale of Aluminum Alloys Shear Modulus25.9 GPa3760 ksi Shear Strength124 MPa18000 psi AA; Typical Electrical Properties Electrical Resistivity4.99e-006 ohm-cm4.99e-006 ohm-cm AA; Typical at 68°F Thermal Properties CTE, linear 68°F23.8 µm/m-°C13.2 µin/in-°F AA; Typical; Average over 68-212°F range. CTE, linear 250°C25.7 µm/m-°C14.3 µin/in-°F Average over the range 20-300ºC Specific Heat Capacity0.88 J/g-°C0.21 BTU/lb-°F Estimated from trends in similar Al alloys. Thermal Conductivity138 W/m-K960 BTU-in/hr-ft²-°F AA; Typical at 77°F Melting Point607 - 649 °C1125 - 1200 °F AA; Typical range based on typical composition for wrought products 1/4 inch thickness or greater Solidus607 °C1125 °F AA; Typical Liquidus649 °C1200 °F AA; Typical Processing Properties Annealing Temperature343 °C650 °F holding at temperature not required Hot-Working Temperature260 - 510 °C500 - 950 °F References for this datasheet. Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistant format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb's disclaimer and terms of use regarding this information. MatWeb data and tools provided by MatWeb, LLC.